Ammonia-stable Y zeolite compositions

ABSTRACT

Highly active, hydrothermally stable and ammonia-stable Y zeolite compositions are disclosed, which compositions are useful as adsorbents, hydrocarbon conversion catalysts, and as acidic supports for catalytic metals. The stabilized Y zeolite composition is prepared from a sodium Y zeolite by a novel sequence of: (1) partial exchange of ammonium ions for sodium ions, (2) steam calcination under controlled conditions of time, temperature and steam partial pressure, and (3) further ion exchange of ammonium ions for sodium ions to reduce the final Na2O content to below about one weight-percent.

" [22] Filed:

[ Dec. 30, 1975 AMMONIA-STABLE Y ZEOLITE COMPOSITIONS [75] Inventor: John W. Ward, Yorba Linda, Calif.

[73] Assignee: Union Oil Company of California,

Los Angeles, Calif.

Oct. 15, 1973 [21] Appl. No.: 406,684

Related US. Application Data [63] Continuation-impart of Ser. Nos. 191,123, Oct. 20, 1971, abandoned, and Ser. No. 236,185, March 20, 1972, Pat. No. 3,781,199.

[52] US. Cl 252/455 Z 51] Int. Cl. B01J 29/06 [58] Field of Search 252/455 2 [56] References Cited UNITED STATES PATENTS 3,257,310 6/1966 Plank et al. 252/455 Z 3,402,996 9/1968 Maher et a1 252/455 Z 6/1969 McDaniel et al 252/455 Z 7/1969 Erickson et a1. 252/455 Z Primary ExaminerCarl F. Dees Attorney, Agent, or FirmLannas S. Henderson; Richard C. Hartman; Dean Sandford [57] ABSTRACT Highly active, hydrothermally stable and ammoniastable Y zeolite compositions are disclosed, which compositions are useful as adsorbents, hydrocarbon conversion catalysts, and as acidic supports for catalytic metals. The stabilized Y zeolite composition is prepared from a sodium Y zeolite by a novel sequence of: (1) partial exchange of ammonium ions for sodium ions, (2) steam calcination under controlled conditions of time, temperature and steam partial pressure, and (3) further ion exchange of ammonium ions for sodium ions to reduce the final Na O content to below about one weight-percent.

32 Claims, 2 Drawing Figures Sheet 1 of 2 3,929,672

US, Patent Dec. 30, 1975 3 3 3 3 3 3 E m Q 3 3 3 NY. 3 3 2 A: T Q I S 223 Sits: n6 2: 1 2 Q2 55$ 6 E2 Q2 $33 0 l a E55 02 Sm 1 2 U 12 oz Sm SE2 4 I 2, mo U535 So 9 55:3 2021335 3:5: 3 1 3 i l E I g l 3 US. Patent Dec. 30, 1975 Sheet2of2 3,929,672

WZDQ mEPZDE KO Si 0 q GNG 3mm :23

w mm 3 8 0m vm ww g1 AMMONIA-STABLE v zEoLrrE COMPOSITIONS RELATED APPLICATIONS BACKGROUND AND SUMMARY OF INVENTION In acid-catalyzed hydrocarbonconversions, the use "of catalysts based on various forms of Y zeolite has become wide-spread. For such purposes, the most desirable forms of Y zeolite are those wherein the original zeolitic sodium ions have been replaced by less basic cations such as hydrogen ions, or polyvalent metal ions such as magnesium or rare earth metal ions. Still another desirable form is sometimes referred to in the literature as the decationized form, which it now appears may actually consist of a form in which part of the exchange sites are actually cation deficient and in which another portion issatisfied by hydrogen ions. To produce the hydrogen and/or decationized forms, the general procedure is to exchange most or all of the original sodium ions with ammonium ions, and the resulting ammonium zeolite is then heated to decompose the zeolitic ammonium ions, first forming a hydrogen zeolite, which may upon further heating be at least partially converted by dehydroxylation to the truly decationized form. The hydrogen form, the decationized form, and the mixed hydrogen-decationized forms will be referred to hereinafter collectively as metal cation deficient Y zeolites.

A problem which was encountered at an early stage in the development of Y zeolite catalysts was that of thermal and hydrothermal stability. The metal-cationdeficient zeolites were found to be in general more active than the polyvalent metal forms, but did not display the hydrothermal stability of the latter. Hydrothermal stability refers to the ability to maintain crystallinity and surface area upon calcination after exposure to water vapor, or upon exposure to water vapor at high temperatures. Severe hydrothermal conditions are often encountered in hydrocarbon conversion processes, either as a result of inadvertent process upsets, or during oxidative regeneration of the catalysts, or in other ways. For these and other reasons most commercial processes such as cracking or hydrocracking utilize a polyvalent metal-stabilized form of the zeolite, even though some degree of activity is thereby sacrificed.

In recent years however this picture has changed somewhat. Several forms of stabilized metal-cationdeficient Y zeolites appear to be available, or at least described in the literature. A common feature involved in the manufacture of such stabilized zeolites appears to be a calcining step, in which an ammonium form of the zeolite is calcined at a relatively high temperature, usually above about 1000F, either in the presence or absence of added steam. This calcination appears to bring about in varying degrees a removal of lattice alumina from the anionic crystal structure, with a resultant shrinkage in the unit cell size to valuesv ranging between about 24.2 and 24.5 A.- Exemplary disclosures of such procedures can be found in U.S. Pat. Nos. 3,293,192 to Mah er et al, 3,449,070 to McDaniel et al, 3,354,077 to I-Iansford, 3,493,519 to Kerr et al, 3,513,108 to Kerr, and 3,506,400 to Eberly et al. My investigations have shown that while the procedures described in each of the foregoing patents are capable of producing ametal-cation-deticient Y zeolite of improved hydrothermal stability, none of such procedures result in a product having the optimum combination of activity, hydrothermal stability, andammonia stability of the zeolites produced herein.

It should be noted that ammonia stability is in many cases as important as hydrothermal stability. In cracking and .hydrocracking processes, the feedstocks often contain substantial quantities of nitrogen compounds which are largely converted to ammonia. These nitrogen compounds, as well as the ammonia, not only sup- .press catalytic activity in varying degrees, but in many cases, especially when water is also present, tend to destroy surface area and crystallinity of the best steamstabilized Y zeolite catalysts of the prior art. Ammonia stability is also essential in catalysts which may, after partial deactivation by metal agglomeration, be subjected to the aqueous ammonia rejuvenation procedure described in U.S. Pat. No. 3,692,692. The ability of the stabilized zeolites described herein to withstand the combined destructive effects of water and ammonia in contrast to other steam-stabilized Y zeolites has not yet been explained.

Briefly summarizing, the critical steps in the manufacture of the stabilized zeolites of my invention are as follows:

1. The initial sodium Y zeolite is subjected to a preliminary ammonium ion exchange to replace most, but not all, of the zeolitic sodium with ammonium ions.

-2. The resulting ammonium-sodium zeolite is then calcined in the presence of steam under controlled conditions of time, temperature and steam partial pressure correlated to reduce the unit cell size of the zeolite to between about 24.40 and 24.64 A.

3. The steam-calcined zeolite is then re-exchanged with ammonium salt to replace at least 25 percent, and preferably at least about percent, of the remaining sodium with ammonium ions.

The chemical and/or physical changes which take place during step (2) of the foregoing procedure appear to be primarily responsible for the unique ammonia stability of the final product. As noted above, the unit cell shrinkage which occurs during this step is believed to involve dealumination of the anionic crystal structure. It now appears however that different types of dealumination can take place during this calcination step, depending upon the sodium content of the, zeolite from step (1 the steam partial pressure in step (2), and perhaps other factors. Certain thermally and/or hydrothermally stabilized Y zeolites of the prior art, even though displaying a unit cell constant within the ranges produced in step (2) herein, have been found to display markedly inferior stability to ammonia. The ammonia-stable compositions of this invention hence appear to be the result of achieving the necessary unit cell shrinkage under the proper conditions, principally sufficient steam atmosphere and a sufficient residual sodium content in the zeolite. A given unit cell shrinkage obtained in a substantially dry atmosphere, or in the substantial absence of zeolitic sodium results in much inferior products as compared to a product of the same unit cell constant produced in the presence of steam and zeolitic sodium ions. It would hence appear that different types of dealumination take place, perhaps at different sites of the anionic crystal structure, depending upon such factors as hydration and cationic influences.

To illustrate the foregoing, US. Pat. No. 3,449,070 I to McDaniel et al discloses a thermal stabilization treatment which apparently is carried out under anhydrous 3,293,192 have been found to be completely unstable to ammonia, due apparently to excessive unit cell shrinkage, as well as a possible deficiency in zeolitic sodium and/or steam during the final calcination treatment. Finally, U.S. Pat. No. 3,354,077 to I-lansford discloses a steam stabilization treatment under conditions of time, temperature, steam pressure and zeolitic sodium content which overlap the critical combination of those conditions required herein, but there is no teaching of an ammoniastable product, or of the critical combination of conditions required to produce such a product. I-Iansford likewise fails to disclose the final ion exchange step required herein.

In addition to high stability, the zeolites of this invention also display unusually high catalytic activity for acid-catalyzed reactions such as cracking, hydrocracking, isomerization, etc, as compared to the stabilized zeolites of the prior art. This is believed to be due pri- 'marily to the fact that thermal stabilization in the presence of both steam and sodium ions brings about a higher degree of stabilization for a given degree of unit cell shrinkage than is achieved in the absence of steam,

or in the absence of sodium ions. The dealumination of the anionic crystal structure which occurs during stabilization, and which apparently brings about unit cell shrinkage, also results in the destruction of catalytically active ion-exchange sites. It is therefore desirable to effect a maximum of stabilization with a minimum of dealumination, or unit cell shrinkage. The process of the present invention achieves this objective to a substantially greater degree than prior art methods.

From the foregoing, it will be apparent that there are critical limitations upon each of the major steps of my process, and that these limitations are cooperatively interrelated with each other in such manner as to produce a final product which is not only hydrothermally stable and ammonia stable, but highly active. To the best of my knowledge, none of the stabilization treatments described in the prior art teach methods for achieving this optimum combination of properties.

For purposes of this invention, a hydrothermally stable zeolite is defined as one which retains at least about 70 percent of its crystallinity after rehydration and calcination for one hour at 900F. An ammoniastable zeolite is defined as one which retains at least about 60 percent of its crystallinity after being subjected to the ammonia stability test hereinafter described.

DETAILED DESCRIPTION The initial sodium Y zeolite starting material utilized herein ordinarily has a SiO /Al O mole ratio between about 3 and 6, and contains about l4 weight-percent of sodium as Na O. In the initial ammonium ion exchange step, the sodium zeolite is digested in conventional manner with an aqueous solution of a suitable ammonium salt such as the chloride, nitrate, sulfate, carbonate, acetate, etc, to replace at least 20 percent, preferably at least about 50 percent but not more than about 95 percent, of the original sodium ions with ammonium ions. The sodium content should be reduced to about 0.6 5 percent, preferably about I 4 percent by weight as Na O. At this point the unit cell size of the zeolite is greater than 24.64 A, usually between about 24.65 and 24.75 A.

Following the initial exchange treatment, I have found that in order to produce a composition having the desired properties outlined above, it is essential that the ammonium-sodium zeolite at this stage be calcined in the presence of steam, as opposed to calcination under anhydrous conditions. As noted above, both high temperatures and a substantial partial pressure of steam are necessary in order to achieve the desired hydrothermal and ammonia-stability via dealumination and unit cell shrinkage. The steam treatment also alters the pore size distribution of the zeolite; the initial Y zeolite has uniform pore diameters of about 10-12 A, while in the steamed product a substantial proportion of the pore volume is in pores of greater than 20 A diameter.

For effective stabilization, the calcination should be carried out while maintaining at least about 0.2 psi water vapor pressure, preferably about 2 I5 psi, and still more preferably about 5 15 psi, for a substantial time at temperatures above 600F. This objective can be realized by any procedure capable of maintaining the desired water vapor partial pressure in contact with the zeolite during at least a substantial portion of the heating. In one modification, the wet zeolite from the exchange step can merely be heated in a covered container so as to retain the water vapor generated therefrom. Alternatively, the zeolite can be introduced into a batch or continuous rotary furnace, or a static bed calcination zone, into which preheated steam or humidified air is introduced. Still another alternative is to heat the wet zeolite, with or without added water, in an autoclave equipped with a pressure relief valve such that super-atmospheric pressures of steam can be maintained therein.

Operative steaming temperatures range between about 600 and I650F, preferably between about 800 and I650F. In any case, the factors of time, temperature and steam partial pressure should be correlated so as to effect the desired stabilization, yet avoid substantial degradation of the crystal structure. The duration of treatment is usually at least about 0.5 minutes, preferably about 10 minutes to about 4 hours, and still more preferably about 0.5 4 hours, but in any event is sufficient to reduce the unit cell size to between about 24.40 and 24.64 A, preferably between about 24.42 and 24.62 A. This reduction in unit cell size is a convenient indicia of the degree of stabilization obtained.

The steam calcined zeolite is then reexchanged with ammonium salt solution under sufficiently severe conditions to reduce the remaining zeolitic sodium content of the zeolite to less than 2, preferably less than about 1, and still more preferably less than about 0.6 weightpercent, as Na O. This ordinarily involves replacing at least 25 percent, preferably at least about percent, of the remaining zeolitic sodium with ammonium ions.

It should be realized that this second exchange step does not introduce any appreciable amount of ammonium ions into the exchange sites which were dehydroxylated in the previous steam calcination step; nearly all of the ammonium ions which go into the zeolite at this point do so by replacing remaining sodium ions. Since for catalytic purposes a substantial ammonium zeolite moiety is desired in the final product for conversion to catalytically active sites of Bronsted acidity, it will be apparent that sufficient sodium should be initially present at the second exchange step, and sufficient of this remaining sodium should be exchanged out with ammonium ion, to provide the ultimately desired Bronsted acidity. For this purpose, the double-exchanged zeolite should contain an amount of ammonium ion corresponding to at least about 5 relative percent, preferably -20 percent, of the original ion exchange capacity of the zeolite. While this remaining ion exchange capacity may appear to represent only a small proportion of the original, potentially active sites, it should be emphasized that these remaining exchange sites are mostly located in the more accessible portions of the crystal structure, and also that a large portion of catalytically active dehydroxylated exchange sites are present.

After drying at temperatures of, e.g., 212 400F, the zeolites produced as above described from highly useful dehydrating agents for gaseous mixtures, particularly gaseous mixtures which may contain ammonia or volatile amines. They are also useful as selective adsorbents for the fractionation of a variety of hydrocarbon mixtures, as well as other organic compounds. They can be used to separate normal paraffins from isoparaffins, aromatic hydrocarbons from paraffins, naphthenes from paraffins, etc. Here again they are especially useful in adsorption processes involving steam regeneration and/or in which ammonia is present during the adsorption or regeneration cycles.

For use as catalysts in acid catalyzed reactions such as alkylation, isomerization, cracking, hydrocracking, etc., the stabilized zeolite from the second ammonium ion exchange step is subjected to calcination at temperatures between about 600 and 1500F, preferably 800 1500F, for a time sufficient to effect substantial deammoniation thereof. Prior to this calcination step, preferably following the second exchange step, the stabilized zeolite is intimately admixed with a finely divided hydrous refractory oxide of a difficultly reducible metal. The term hydrous" is used to designate oxides having structural surface hydroxyl groups detectable by infra red analysis. The preferred oxides are alumina, silica, magnesia, beryllia, zirconia, titania, thoria, chromia, and combinations thereof such as silica-alumina, silica-magnesia, and the like. Naturally occurring clays comprising silica and alumina may also be utilized, preferably after acid treatment. The resulting mixtures may contain between about 0.5 and 98 weight-percent of zeolite, preferably at least about 2 weight-percent, and generally about 2 to about 80 weight-percent, based on the combined dry weight of the zeolite and the metal oxide. The metal oxide can be combined with the zeolite as a hydrous sol or gel, as an anhydrous activated gel, a spray dried powder or a calcined powder. In one modification a sol or solution of the metal oxide precursor such as an alkali metal silicate or aluminate can be precipitated to form a gel in the presence of the zeolite.

When less hydrous forms of the metal oxide are combined with the zeolite, essentially any method of effecting intimate admixture of the components may be utilized. One such method is mechanical admixture, e.g., mulling, which involves admixing the zeolite in the form of a powder with the slightly hydrous, finely divided form of the metal oxide. Minor amounts of water, with or without an acidic peptizing agent such as a strong mineral acid, are usually added to facilitate admixture.

After admixing the hydrous oxide with the zeolite component, it is normally preferable at this point to consolidate the mixture into the granular shape desired for the final catalyst. Conventional tableting, prilling, or extruding procedures may be utilized to produce tablets, prills or extrudate pellets having a diameter of about 1/32 inch to inch. Other conventional pelleting aids may be added such as lubricants, binders, diluents, etc. Macro-granules of this nature are ordinarily utilized in fixed bed processing, but other processes such as fluid catalytic cracking require micro-granules produced for example by conventional spray drying techniques.

It is preferred to maintain a relatively anhydrous environment during this second calcination. If there is substantial water vapor partial pressure during this step, the final catalyst is usually less active than those produced in the substantial absence of water vapor. Accordingly, this calcination is'preferably conducted in the presence of less than 2, and preferably less than about 1, psi of water vapor. The calcination may be regarded as complete when substantially all ammonia and physically adsorbed water have been expelled from the catalyst, which, depending on the temperature employed, may range between about 10 minutes and 12 hours or more. The overall severity of this calcination should be controlled to prevent any substantial further shrinkage in the unit cell size of the zeolite; it is essential that the final unit cell size be above 24.40 A, preferably above about 24.44 A.

For use in hydrogenative conversion processes such as hydrocracking, hydroisomerization, etc, the necessary metal hydrogenation component may be distributed selectively onthe zeolite component of the catalyst, or on the refractory oxide component. Alternatively it may be distributed more or less equally on both components. Effective hydrogenation components comprise the Group VIB and/or Group VIII metals and their oxides and/or sulfides, with or without other metals such as rhenium. Operative proportions (based on free metal) may range between about 0.1 percent and 30 percent by weight, depending upon the type of metal or metals selected, and the desired activity. In the case of the Group VIII noble metals, amounts in the range of 0.1 to about 2 percent will normally be employed; the iron group metals, iron, cobalt and nickel, are normally utilized in proportions of about [-10 weight-percent; the Group VIB metals will normally be utilized in proportions of about 3-20 weight-percent. Preferred hydrogenating metals are palladium, platinum, nickel, cobalt, tungsten and molybdenum. Particularly preferred are palladium or platinum, or combinations of nickel and/or cobalt with molybdenum and- /or tungsten.

The hydrogenating component may be added to the catalyst at any desired stage in its manufacture. Preferred methods include impregnation and/or ion-exchange of soluble metal salts into the powdered zeolite after the second ammonium ion exchange, or into the catalyst pellets prior to the final calcination step. Other methods include mixing of soluble or insoluble comg fg g gi f Preferred Ran e pounds of the desired metal or metals with the powg g 5 Tem erature, T. 450 850 550 800 dered zeol1te hydrous metal oxide mixture prior to Totafpressme psigm 3000 600 2000 extruding or pelletmg. LHSV 0,2 10 1 5 In addition to their low sodium content, the catalysts g/ i CF/ -5 15 1 0 lk lf d lz i also i ly free of other l l "At least about 75 percent of which should be hydrogen partial pressure. itic a an an a a ine eart meta cations, as we as rare earth metals. The resence of an of these zeolitic 10 metal components in iimounts excezding about l-2 It Is pamcuiaily noieworthy that.the hydrocrackmg weight-percent is found to substantially reduce the Catalysts of thlsmverinon a especlagy usefulforlow activity of the catalyst for acid catalyzed reactions such g ijs fi 5 $2 3; :5 1 6 6b g gg g gii z zi as cracking, hydrocracking, isomerization, etc. 6 e a u a p y h h b The base zeolite compositions described above, or i lower rates at Pressures t an t e est the zeolite-amorphous oxide combinations, are found g ii sz g f 2133 Contains more to be highly active for a wide variety of acid catalyzed th n g f ni nitro en an inte m1 hydrocarbon conversions, e.g., cracking, isomerization an a ppm 0 .orga c g f of n-paraffins to isoparaffins, isomerization of alkyl hdrfimnghydrcrackmg systefmfmay f f n aromatics, transalkylation of alkyl aromatics, alkylathis profiedure the .feedstock Subjects tion, etc. For these purposes a hydrogenation compoconventional catalynqhydrottmmg trefatment and t e nent is not ordinarily necessary although in paraffin effluent i wlihout mteri/enmg treatment to isomerization a hydrogenation component is someremoye ammoma 1S .dlrecfly Subjected to the above times desirable. For catalytic cracking, the preferred i z E T Tg cited to demon compositions comprise about 2 to weight-percent of 25 e o 0 g exa p i the zeolite component and 75 98 weight percent of strate the superlor ammoma stab1l1ty and hydrothermal the refractory oxide component. In fluid catalytic Stability of the catalysts of thls Invention cracking employing such catalysts, excellent conver- EXAMPLES 1 12 sions of gas oils to gasoline are obtainable under con- In th Se exam [es the Startin material was a ventional cracking conditions, including temperatures e p g of about 100001;. at p g Since catalytic stantially 100 percent crystalline ammonium Y zeolite cracking feedstocks ordinarily contain from about containing aboin weilght'peicem of resldualzeolmc 10-2000 ppm of organic nitrogen, the ammonia-stable g z i mt f i r i ii?? g catalysts of this invention find particular utility in that a p 9 o a I g ma e a e e u J c 0 area following steps in sequence:

The catalysts containing a hydrogenating component 1 gg lgz i izifi under vanous conditions are particularly useful for hydrocracking. Feedstocks a which y be directly subjected to hydrocracking 2 Standard X-ray analysis for crystallimty and unit herein include in general any mineral oil fraction boilcell i ing between about 200 and 14000}: preferably 3 40 3 Identical ammonium lOl'l exchange treatments with 12000]: For best results the feed should contain less ammonium nitrate solutions to reduce the zeolitic than about 10 ppm, preferably less than about 5 ppm of 4 :2 :3 a??? 8? 1%;: gf zz lggtgz i lg organic nitrogen. The usual feedstocks include straight Co I m t 25 1 ht em run gas oils, coker distillate gas oils, deasphalted crude 5 g g i anal oils, cycle oils derived from catalytic or thermal crack- 6 Cale. ati n atygoooFyf 1 as l ing operations, and the like, any of which may if neces- 7 S t I P (t d t r sary have been subjected to suitable pretreatment to il ;;g;:? q y 0 e e reduce the organic nitrogen content to the desired 8 Reh drition to about 20 l ht ercent H O fol levels. The hydrocracking can be successfully continloweyd b reammoniation to saiurzfiion with ued for periods of at least about 60 days in the presence NH at z mm 6 ature and removal excess of between about 5 and 5,000 ppm, but more conven- 3 m r tionally between about 50 2000 pp y weight of ammonia by purging with nitrogen for 16 hours at ammonia, based on feed. The usual products from 9 g ig g fgg x gzh 930: for one hourin flowin hydrocracking include gasoline, diesel fuels, turbine air and a g fuels, r0 ane-butane fuels and the like. Suitable h drocra ckiiig conditions may be selected within tli e Standard 'i anglysls for crystanmlty (to deterfonowin ran es mine ammonia-stability).

g g The results of the tests were as follows:

Table 1 Initial Calcination Percent of Crystallinity H2O Unit Cell Retained at: Example Hrs. Temp., F psi Size, A Step 7 Step 10 Table l-continued lnitial Calcination Percent of Crystallinity 11,0 Unit Cell Retained at: Example Hrs. Temp., F psi Size, A Step 7 Step 10 l l l 1292 24.578 56 72 12 l 1472 -0 24.486 70 70 Based on crystallinity found at step (5). ""Based on crystallinity found at step (7). "Average of 5 runs.

.- 'Average of 3 runs.

The above data for crystallinity retained at step (10) (Examples l-lO) is plotted versus unit cell size in the accompanying FIG. 1, giving curve 'A,'which represents the percent of crystallinity which survived the ammonia stability test. Curve B depicts the analogous data for Examples 1 l and 12. It is evident that, for a given unit cell size, the steam calcination of Examples 1-10 gives products of substantially superior ammonia-stability, as compared to the dry calcination of Examples 11 and 12'. The succeeding Examples 13-15 will show however that this desirable result is not obtained when the zeolite is essentially free of sodium during the steam calcination.

The above data for crystallinity retained at step (7) (Examples l-lO) is plotted versus unit cell size in FIG. 2, giving curve D, which represents the percent of crystallinity which survived the hydrothermal stability test. Curve E depicts the analogous data for Examples 11 and 12. It is evident that to obtain a given degree of hydrothermal stability, considerably more unit cell shrinkage (and loss of exchange sites) is required when steam is not present during the initial calcination.

EXAMPLES 13 1s In these Examples the starting material was a substantially 100 percent crystalline ammonium Y zeolite which had been exhaustively ion-exchanged to a sodium content of 0.04 weight-percent as Na. Three samples of this material were subjected to the following steps in sequence:

1 Steam calcination under conditions tabulated below;

2 Standard X-ray analysis for crystallinity and unit cell size;

3 Rehydration to about weight-percent H O, followed by reammoniation to saturation with gaseous NH at room temperature and removal of excess ammonia by purging with nitrogen for l6'hours;

4 Calcination at about 930F for 1 hour in flowing air; and

5 Standard X-ray analysis for crystallinity (to determine ammonia-stability).

The results of the tests were as follows:

which represents the percent of crystallinity which survived the ammonia-stability test. It is evident that in the absence of sodium, steam calcination is a relatively ineffective stability treatment.

Thefollowing Examples 16-28 are'cited to illustrate the superior hydrocracking activity ofthe catalysts of this invention, but are not to be construed as limiting in scope:

EXAMPLES 16-19 Preparation of Catalysts Catalyst A: Sodium Y zeolite was ion exchanged with ammonium sulfate solution until the sodium content was reduced to 1.5- 2 weight-percent Na O. The resulting ammonium-sodium zeolite was then calcined in flowing steam for 1 hour at 1292F and then further ion exchanged with ammonium salt solution until the sodium content was reduced to less than 0.2 percent Na O. The resulting product was'then slurried in dilute ammonium hydroxide, into which a solution of palladium chloride in dilute ammonium hydroxide was slowly stirred. The product was washed free of chloride, mixed with 20 weight-percent (dry basis) of acidpeptized alumina, extruded into 6 inch pellets, dried and calcined at about 900F for 1 hour. The finished catalyst contained about-0.5 weight-percent Pd, and the unit cell size of the zeolite was 24.483 A.

Catalyst B: A sample of Davison ultrastable zeolite Z-l4US was composited with 0.5 weight-percent Pd and 20 percent A1 0 as described above to give a product with a unit cell size of 24.337 A. The Z-l4US zeolite was prepared by the double-exchange, doublecalcination procedure described in US. Pat. No. 2,293,192, i.e., with a first ammonium ion exchange to reduce the sodium content to about 3 weight-percent Na O followed by calcination at about l00OF, reexchange to reduce the sodium content to below 1 percent Na O, and a final calcination at about l,56 0F.

. .Catalyst C: Sodium Y zeolite was ammonium ion exchanged, steam calcined and again ammonium 'ion exchanged as described in the catalyst A procedure. The resulting product was then dried and mulled with acid-peptized alumina gel, nickel carbonate, ammo- Table 2 Calcination 11,0 Unit Cell Percent of crystallinity Example Hrs. Temp., F psi Size, A Retained at Step 5" 13 l 1000 15 24.472 62 14 l 1200 15 24.391 0 l5 1 1300 15 24.380 0 "Based on crystallinity found at step (2).

The above data for crystallinity retained'at step (5) is plotted versus unit cell size in FIG. 1, giving Curve C,

nium heptamolybdate and sufficient concentrated nickel nitrate solution to provide a moist, extrudable 1 1 paste. The proportions of ingredients were such as to provide a finished catalyst of about the following weight-percent composition:

Zeolite 60 A1 gel 20 M00; 1 5 MO 5 The mulled mixture was then extruded into 1/16 inch pellets, dried and calcined at 900F for 1 hour.

Catalyst D was a more conventional Pd-Y zeolite catalyst comprising a copelleted composite of weight-percent alumina, 80 weight-percent of a magnesium back-exchanged hydrogen Y zeolite (3 weightpercent MgO), and 0.5 weight-percent of Pd. This catalyst had not been subjected to hydrothermal stabilization, but was hydrothermally stable by virtue of its zeolitic magnesium content.

EXAMPLES 20-23 Catalysts A, B, C and D above were ground to 14-20 mesh particles and compared for hydrocracking activity, using as feed an unconverted gas oil derived from a previous hydrofining-hydrocracking run, having an API gravity of 38, and a boiling range of 360-870F, with about 12 percent boiling below 400F. For test purposes, the feed was doped with 0.5 weight-percent sulfur as thiophene and 0.2 weight-percent nitrogen as tertbutylamine. Each catalyst was tested at hydrogen pressures of about 1,450 and 500 psi, each run being carried out at LHSV 1.7, H /oil ratio of 8,000 SCF/B, with temperatures periodically adjusted to maintain a total liquid product gravity of 47AP1. By previously established correlations, this product gravity corresponds to a conversion of about 38 volume-percent to C -400F gasoline (after deducting the 12 volume-percent of feed which boiled below 400F). The respective temperatures required to maintain this conversion after 100 hours on stream were as follows:

Table 3 Catalyst Temperatures for 38% Conversion, F

1450 psi 00 psi A 689 736 B 712 742 C 707 724 D 722 840 "Catalyst was deactivating so rapidly that only about 23 percent conversion was being obtained. TlR was about 22F per day with no apparent leveling out.

EXAMPLES 24-26 Catalysts A, B and D were tested as described in Examples 20-23, using the same feed except for the omission of the added tert-butylamine. In this case however, temperatures were adjusted to maintain a product gravity of 49.5APl, which corresponds to a 12 conversion of about 48 volume-percent to C -400F gasoline. At 1450 psi, the results were as follows:

It will be seen that at 1,450 psi, catalyst A was substantially superior to either of the prior art catalysts B or D.

EXAMPLE 27 Catalyst C was used to hydrocrack another hydrofined gas oil having an API gravity of 35 and a boiling range of 1757l6F, with about 9 percent boiling below 400F. The feed contained about 1 ppm nitrogen and 12 ppm sulfur.

The catalyst was presulfided with a H /H S mixture and evaluated at 950 psig, and at 3.0 and 1.7 LHSV. H loil ratio was 8000 SCF/B. The temperature was periodically adjusted to maintain a total product gravity of 60.5API, corresponding to a conversion of about volume percent per pass to C.,-400F gasoline (after deducting the 9 volume-percent of feed boiling below 400F).

After 250 hours on stream at 3.0 LHSV, the temperature required to maintain conversion was about 660F and the deactivation rate was about 25F per day. After 300 hours on stream the deactivation rate was about 1.2F per day. After a further 160 hours on stream at 1.7 LHSV the deactivation rate was less than 0.3F per day, and the temperature required to maintain 80 percent conversion to 400F end point gasoline was 642F.

From this data, it can be deduced that a commercial operation of greater than six months duration is feasible using the above conditions.

EXAMPLE 28 Operation as in Example 27 was continued at 700 psig and 1.7 LHSV. After a further hours on stream, the required temperature for 80 percent conversion was 670F, and the deactivation rate was less than'0.5F per day.

Examples 24-28 demonstrate that, even in the absence of ammonia, the catalysts of this invention are substantially more active than the prior art catalysts.

The following claims and their obvious equivalents are intended to define the true scope of the invention:

1 claim:

1. A catalyst composition comprising a minor proportion of a hydrogenation component selected from the class consisting of the Group VIB and Group VIII metals and their oxides and sulfides intimately composited with a hydrothermally stable, ammonia-stable Y zeolite base, said Y zeolite base having been prepared by the steps of:

l calcining an ammonium sodium Y zeolite containing about 0.6 5 weight-percent of sodium as Na O, said calcining being carried out at a temperature between about 600 and 1650F in contact with at least about 0.2 psi of water vapor for a sufficient time to substantially reduce the unit cell size of said zeolite and bring it to a value between about 24.40 and 24.64 A;

t 13 a 2 subjecting the calcined zeolite to further ammonium ion exchange under conditions adjusted to replace at least about 25 percent of its residual zeolitic sodium ions with ammonium ions and produce a product containing less than about 1 weightpercent Na O; consolidating the product from step (2) into granules having intimately admixed therein a finely divided hydrous oxide selected from the class consisting of alumina, silica, magnesia, titania, zirconia, thoria, beryllia, chromia, clays and mixtures thereof; and I calcining the granules at a temperature between about 600 and 1500F for a time sufficient to effect substantial deammoniation, but insufficient to reduce the unit cell size of the zeolite to below about 24.40 A. v

2. A catalyst composition as defined in claim 1 wherein step (4) .is carried out under substantially dry conditions.

3. A catalyst composition as defined in claim 1 wherein'said hydrogenation component is palladium.

4. A catalyst composition as defined in claim 1 wherein said hydrogenation component comprises nickel and molybdenum as free metals, oxides or sulfides. Y

5. A catalyst composition as defined in claim 1 wherein said hydrous oxide is essentially alumina.

6. A catalyst composition as defined in claim 5 wherein said hydrogenation component is palladium.

7. A catalyst composition as defined inb'claim 5 wherein said hydrogenation component comprises nickel and molybdenum as free metals, oxides or sulfides.

8. A catalyst composition comprising a minor proportion of a hydrogenation component selected from the class consisting of the Group VB and Group VIII metals and their oxides and sulfides intimately, composited with a hydrothermally stable, ammonia-stable Y zeolite base, said Y zeolite base having been prepared by the steps of: 1

1 calcining an ammonium-sodium Y zeolite containing about 1 4 weight-percent of sodium as Na O, said calcining being carried out at a temperature between about 800 and 1650F in contact with between about 2-l5 psi of water vapor for a sufficient time to substantially reduce the unit cell size of said zeolite and bring it to a value between about 24.42 and 24.62 A; subjecting the calcined zeolite to further ammonium ion exchange under conditions adjusted to replace at least about 70 percent of its residual zeolitic sodium ions with ammonium ions and produce a product containing less than about 0.6 weight-percent Na O;

3 consolidating the product from step (2) into granules having intimately admixed therein a finely divided hydrous oxide selected from the class consisting of alumina, silica, magnesia, titania, zirconia, thoria, beryllia, chromia, clays and mixtures thereof; and

calcining the granules at a temperature between about 800 and l500F for a time sufficient to effect substantial deammoniation, but insufficient to reduce the unit cell size of the zeolite to below about 24.40 A.

9. A catalyst composition as defined in claim 8 wherein step (4). is carried out under substantially dry conditions.

10. A catalyst composition as defined in claim 8 .wherein said hydrogenation component is palladium.

wherein said hydrogenation component is palladium.

14. A catalyst composition as defined in claim 12 wherein said hydrogenation component comprises nickel and molybdenum as free metals, oxides or sulfides.

l5. A hydrothermally stable, ammonia-stable Y zeolite composition prepared by the steps of:

l calcining an ammonium-sodium Y zeolite containing about 0.6 5 weight-percent of sodium as Na' O, said calcining being carried out at a temperature between about 600 and 1650F in contact with at least about 0.2 psi of water vapor for a sufficient time to substantially reduce the unit cell size of said zeolite and bring it to a value between about 24.40 and 24.64 A; and subjecting the calcined zeolite to further ammonium ion exchange under conditions adjusted to replace at least about 25 percent of its residual zeolitic sodium ions with ammonium ions and produce a final product containing less than about 1 weight-percent Na O.

16. A catalyst composition prepared by the steps of: (a) consolidating the product from claim 15 into granules having intimately admixed therein a finely divided hydrous oxide selected from the class consisting of alumina, silica, magnesia, titania, zirconia, thoria, beryllia, chromia, clays and mixtures thereof; and (b) calcining the granules at a temperature between about 600,and 1500F for a time sufficient toeffect substantialdeammoniation, but insufficient to reduce the unit cell size of the zeolite to below about 24.40 A. v

17. A catalyst composition as defined in claim 16 wherein said hydrous oxide is essentially alumina.

18. A catalyst composition as defined in claim 16 wherein step (b) is carried out under substantially dry conditions.

19. A hydrothermally stable, ammonia-stable Y zeolite composition prepared by the steps of:

l calcining an ammonium-sodium Y zeolite containing about I 4 weight-percent of sodium as Na O, said calcining being carried out at a temperature between about 800 and 1650F in contact with between about 2-15 psi of water vapor for a sufficient time to substantially reduce the unit cell size of said zeolite and bring it to a value between about 24.42 and 24.62 A; and subjecting the calcined zeolite to further ammonium ion exchange under conditions adjusted to replace at least about percent of its residual zeolitic sodium ions with ammonium ions and produce a final product containing less than about 0.6 weight-percent Na O.

20. A catalyst composition prepared by the steps of: a consolidating the product from claim 19 into granules having intimately admixed therein a finely divided hydrous oxide selected from the class con- 15 sisting of alumina, silica, magnesia, titania, zirconia, thoria, beryllia, chromia, clays and mixtures thereof; and

b calcining the granules at a temperature between about 800 and l500F for a time sufficient to effect substantial deammoniation, but insufficient to reduce the unit cell size of the zeolite to below about 24.40 A.

21. A catalyst composition as defined in claim 20 wherein step (b) is carried out under substantially dry conditions.

22. A catalyst composition as defined in claim 20 wherein said hydrous oxide is essentially alumina.

23. A method for the manufacture of a hydrothermally stable, ammonia-stable Y zeolite composition,

- which comprises:

1 calcining an ammonium-sodium Y zeolite containing about 0.6 weight-percent of sodium as Na O, said calcining being carried out at a temperature between about 600 and l650F in contact with at least about 0.2 psi of water vapor for a sufficient time to substantially reduce the unit cell size of said zeolite and bring it to a value between about 24.40 and 24.64 A; and

subjecting the calcined zeolite to further ammonium ion exchange under conditions adjusted to replace at least about 25 percent of its residual zeolitic sodium ions with ammonium ions and produce a final product containing less than about 1 weight-percent Na- O.

24. A method as defined in claim 23 including the further steps of:

3 consolidating the product from step (2) into granules having intimately admixed therein a finely divided hydrous oxide selectedfrom the class consisting of alumina, silica, magnesia, titania, zirconia, thoria, beryllia, chromia, clays and mixtures thereof; and calcining the granules at a temperature between about 600 and l500F for a time sufficient to effect substantial deammoniation, but insufficient to reduce the unit cell size of the zeolite to below about 24.40 A.

16 25. A method as defined in claim 24 wherein said hydrous oxide is essentially alumina.

26. A method as defined in claim 24 wherein step (4) is carried out under substantially dry conditions. 5 27. A method as defined in claim 23wherein step l is carried out with the zeolite in contact with flowing steam.

28. A method for the manufacture of a hydrothermally stable, ammonia-stable Y zeolite composition, which comprises:

1 calcining an ammonium-sodium Y zeolite containing about 1 4 weight-percent of sodium as Na O, said calcining being carried out at a temperature between about 800 and 1650F in contact with between about 2-15 psi of water vapor for a sufficient time to substantially reduce the unit cell size of said zeolite and bring it to a value between about 24.42 and 24.62 A; and

2 subjecting the calcined zeolite to further ammonium ion exchange under conditions adjusted to replace at least about 70 percent of its residual zeolitic sodium ions with ammonium ions and produce a final product containing less than about 0.6 weight-percent Na O.

29. A method as defined in claim 28 including the further steps of:

3 consolidating the product from step (2) into granules having intimately admixed therein a finely divided hydrous oxide selected from the class consisting of alumina, silica, magnesia, titania, zirconia, thoria, beryllia, chromia, clays and mixtures thereof; and

4 calcining the granules at a temperature between about 800 and l500F for a time sufficient to effect substantial deammoniation, but insufficient to reduce the unit cell size of the zeolite to below about 24.40 A.

30. A method as defined in claim 29 wherein said hydrous oxide is essentially alumina.

31. A method as defined in claim 29 wherein step (4) is carried out under substantially dry conditions.

32. A method as defined in claim 28 wherein step l is carried out with the zeolite in contact with flowing steam. 

1. CALCINING AN AMMONIUM-SODIUM Y ZEOLITE CONTAINING ABOUT 0.6-5 WEIGHT-PERCENT OF SADIUM Y ZEOLITE CONTAINING CALCINING BEING CARRIED OUT AT A TEMPERATURE BETWEEN ABOUT 600*F IN CONTACT WITH AT LEAST ABOUT 0.2 PSI. OF WATER VAPOR FOR A SUFFICIENT TIME TO SUBSTANTIALLY REDUCE THE UNIT CELL SIZE OF SAID ZEOLITE AND BRING IT TO A VALUE BETWEEN ABOUT 24.40 AND 24.64 A; AND S
 2. SUBJECTING THE CALCINED ZEOLITE TO FURTHER AMMONIUM ION EXCHANGE UNDER CONDITIONS ADJUSTED TO REPLACE AT LEAST ABOUT 25 PERCENT OF ITS RESIDUCAL ZEOLITIC SODIUM IONS WITH AMMONIUM IONS AND PRODUCE A FINAL PRODUCT CONTAINING LESS THAN ABOUT 1 WEIGHT-PERCENT NA2O.
 1. A CATALYST COMPOSITION COMPRISING A MINOR PROPORTION OF IF HYDROGENATION COMPONENT SELECTED FROM THE CLASS CONSISTING OF THE GROUP VIB AND GROUP VIII METALS AND THEIR OXIDES AND SULFIDES INTIMATELY COMPOSITED WITH A HYDROTHERMALLY STABLE, AMMONIA-STABLE Y ZEOLITE BASE, AND Y ZEOLITE BASE HAVING BEEN PREPARED BY THE STEPS OF*
 1. CALCINING AN AMMONIUM SODIUM Y ZEOLITE CONTAINING ABOUT 0.6-5 WEIGHT-PERCENT OF SODIUM AS NA2O, SAID CALCINING BEING CARRIED OUT AT A TEMPERATURE BETWEEN ABOUT 600* AND 1650*F IN CONTACT WITH AT LEAST ABOUT 0.2 PSI OF WATER VAPOR FOR A SUFFICIENT TIME TO SUBSTANTIALLY REDUCE THE UNIT CELL SIZE OF SAID ZEOLITE AND BRING IT TO A VALUE BETWEEN ABOUT 24.40 AND 24.64 A;
 2. SUBJECTING THE CALCINED ZEOLITE TO FURTHER AMMONIUM ION EXCHANGE UNDER CONDITIONS ADJUSTED TO REPLACED AT LEAST ABOUT 25 PERCENT OF ITS RESIDUAL ZEOLITIC SODIUM IONS WITH AMMONIUM IONS AND PRODUCE A PRODUCT CONTAINING LESS THAN ABOUT 1 WEIGHT-PERCENT NA2O
 2. A catalyst composition as defined in claim 1 wherein step (4) is carried out under substantially dry conditions.
 3. A catalyst composition as defined in claim 1 wherein said hydrogenation component is palladium.
 3. CONSOLIDATING THE PRODUCT FROM STEP (2) INTO GRANULES HAVING INTIMATELTY ADMIXED THEREIN A FINELY DIVIDED HYDROUS OXIDE SELECTED FROM THE CLASS CONSISTING OF ALUMINA, SILICA, MAGNESIA, TITANIA, ZIRCONIA, THORIA, BERYLLIA, CHROMIA, CLAYS AND MIXTURES THEREOF; AND
 4. CLACINING THE GRANULES AT A TEMPERATURE BETWEEN ABOUT 600*F FOR A TIME SUFFICIENT TO EFFECT SUBSTANTIAL DEAMMONIATION, BUT INSUFFICIENT TO REDUCE THE UNIT CELL SIZE OF THE ZEOLITE TO BELOW ABOUT 24.40 A.
 4. A catalyst composition as defined in claim 1 wherein said hydrogenation component comprises nickel and molybdenum as free metals, oxides or sulfides.
 5. A catalyst composition as defined in claim 1 wherein said hydrous oxide is essentially alumina.
 6. A catalyst composition as defined in claim 5 wherein said hydrogenation component is palladium.
 7. A catalyst composition as defined in claim 5 wherein said hydrogenation component comprises nickel and molybdenum as free metals, oxides or sulfides.
 8. A catalyst composition comprising a minor proportion of a hydrogenation component selected from the class consisting of the Group VIB and Group VIII metals and their oxides and sulfides intimately composited with a hydrothermally stable, ammonia-stable Y zeolite base, said Y zeolite base having been prepared by the steps of: 1 calcining an ammonium-sodium Y zeolite containing about 1 - 4 weight-percent of sodium as Na2O, said calcining being carried out at a temperature between about 800* and 1650*F in contact with between about 2-15 psi of water vapor for a sufficienT time to substantially reduce the unit cell size of said zeolite and bring it to a value between about 24.42 and 24.62 A; 2 subjecting the calcined zeolite to further ammonium ion exchange under conditions adjusted to replace at least about 70 percent of its residual zeolitic sodium ions with ammonium ions and produce a product containing less than about 0.6 weight-percent Na2O; 3 consolidating the product from step (2) into granules having intimately admixed therein a finely divided hydrous oxide selected from the class consisting of alumina, silica, magnesia, titania, zirconia, thoria, beryllia, chromia, clays and mixtures thereof; and 4 calcining the granules at a temperature between about 800* and 1500*F for a time sufficient to effect substantial deammoniation, but insufficient to reduce the unit cell size of the zeolite to below about 24.40 A.
 9. A catalyst composition as defined in claim 8 wherein step (4) is carried out under substantially dry conditions.
 10. A catalyst composition as defined in claim 8 wherein said hydrogenation component is palladium.
 11. A catalyst composition as defined in claim 8 wherein said hydrogenation component comprises nickel and molybdenum as free metals, oxides or sulfides.
 12. A catalyst composition as defined in claim 8 wherein said hydrous oxide is essentially alumina.
 13. A catalyst composition as defined in claim 12 wherein said hydrogenation component is palladium.
 14. A catalyst composition as defined in claim 12 wherein said hydrogenation component comprises nickel and molybdenum as free metals, oxides or sulfides.
 15. A HYDROTHERMALLY STABLE, AMMONIA-STABLE Y ZEOLITE COMPOSITION PREPARED BY THE STEPS OF:
 16. A catalyst composition prepared by the steps of: (a) consolidating the product from claim 15 into granules having intimately admixed therein a finely divided hydrous oxide selected from the class consisting of alumina, silica, magnesia, titania, zirconia, thoria, beryllia, chromia, clays and mixtures thereof; and (b) calcining the granules at a temperature between about 600* and 1500*F for a time sufficient to effect substantial deammoniation, but insufficient to reduce the unit cell size of the zeolite to below about 24.40 A.
 17. A catalyst composition as defined in claim 16 wherein said hydrous oxide is essentially alumina.
 18. A catalyst composition as defined in claim 16 wherein step (b) is carried out under substantially dry conditions.
 19. A hydrothermally stable, ammonia-stable Y zeolite composition prepared by the steps of: 1 calcining an ammonium-sodium Y zeolite containing about 1 - 4 weight-percent of sodium as Na2O, said calcining being carried out at a temperature between about 800* and 1650*F in contact with between about 2-15 psi of water vapor for a sufficient time to substantially reduce the unit cell size of said zeolite and bring it to a value between about 24.42 and 24.62 A; and 2 subjecting the calcined zeolite to further ammonium ion exchange under conditions adjusted to replace at least abouT 70 percent of its residual zeolitic sodium ions with ammonium ions and produce a final product containing less than about 0.6 weight-percent Na2O.
 20. A catalyst composition prepared by the steps of: a consolidating the product from claim 19 into granules having intimately admixed therein a finely divided hydrous oxide selected from the class consisting of alumina, silica, magnesia, titania, zirconia, thoria, beryllia, chromia, clays and mixtures thereof; and b calcining the granules at a temperature between about 800* and 1500*F for a time sufficient to effect substantial deammoniation, but insufficient to reduce the unit cell size of the zeolite to below about 24.40 A.
 21. A catalyst composition as defined in claim 20 wherein step (b) is carried out under substantially dry conditions.
 22. A catalyst composition as defined in claim 20 wherein said hydrous oxide is essentially alumina.
 23. A method for the manufacture of a hydrothermally stable, ammonia-stable Y zeolite composition, which comprises: 1 calcining an ammonium-sodium Y zeolite containing about 0.6 -5 weight-percent of sodium as Na2O, said calcining being carried out at a temperature between about 600* and 1650*F in contact with at least about 0.2 psi of water vapor for a sufficient time to substantially reduce the unit cell size of said zeolite and bring it to a value between about 24.40 and 24.64 A; and 2 subjecting the calcined zeolite to further ammonium ion exchange under conditions adjusted to replace at least about 25 percent of its residual zeolitic sodium ions with ammonium ions and produce a final product containing less than about 1 weight-percent Na2O.
 24. A method as defined in claim 23 including the further steps of: 3 consolidating the product from step (2) into granules having intimately admixed therein a finely divided hydrous oxide selected from the class consisting of alumina, silica, magnesia, titania, zirconia, thoria, beryllia, chromia, clays and mixtures thereof; and 4 calcining the granules at a temperature between about 600* and 1500*F for a time sufficient to effect substantial deammoniation, but insufficient to reduce the unit cell size of the zeolite to below about 24.40 A.
 25. A method as defined in claim 24 wherein said hydrous oxide is essentially alumina.
 26. A method as defined in claim 24 wherein step (4) is carried out under substantially dry conditions.
 27. A method as defined in claim 23 wherein step (1) is carried out with the zeolite in contact with flowing steam.
 28. A method for the manufacture of a hydrothermally stable, ammonia-stable Y zeolite composition, which comprises: 1 calcining an ammonium-sodium Y zeolite containing about 1 - 4 weight-percent of sodium as Na2O, said calcining being carried out at a temperature between about 800* and 1650*F in contact with between about 2-15 psi of water vapor for a sufficient time to substantially reduce the unit cell size of said zeolite and bring it to a value between about 24.42 and 24.62 A; and 2 subjecting the calcined zeolite to further ammonium ion exchange under conditions adjusted to replace at least about 70 percent of its residual zeolitic sodium ions with ammonium ions and produce a final product containing less than about 0.6 weight-percent Na2O.
 29. A method as defined in claim 28 including the further steps of: 3 consolidating the product from step (2) into granules having intimately admixed therein a finely divided hydrous oxide selected from the class consisting of alumina, silica, magnesia, titania, zirconia, thoria, beryllia, chromia, clays and mixtures thereof; and 4 calcining the granules at a temperature betwEen about 800* and 1500*F for a time sufficient to effect substantial deammoniation, but insufficient to reduce the unit cell size of the zeolite to below about 24.40 A.
 30. A method as defined in claim 29 wherein said hydrous oxide is essentially alumina.
 31. A method as defined in claim 29 wherein step (4) is carried out under substantially dry conditions.
 32. A method as defined in claim 28 wherein step (1) is carried out with the zeolite in contact with flowing steam. 